PRESSURE VESSELS PLATES (ASTM A285, A515, A516)
BS EN 10028-2 : 1993 Flat products made of steel for pressure purposes
BS EN 10028-3 : 1993 Flat products made of steel for pressure purposes
DIN 17155 - EN 10083 HEAT Resistant Plates

美国标准

(Properties minima unless stated)

No.	Title 品种	Grade 钢号	Chemical Composition 化学成份 %					Treatment⁵⁾ 加工处理	Tensile Strength 抗拉强度 ksi(MPa)	Yield Stress⁴⁾ 屈服强度ksi(MPa)	Elongation 伸长率%		Thickness 厚度 t in
			(maxima unless stated)
			C	Si	Mn	P	S				8 in	2 in
A285-90	Pressure vessel plates, carbon steel, low and intermediate tensile strength	A	0.17	-	0.90	0.035	0.035	-	45/65 (310/450)	24 (165)	27¹⁾	30	t£2
		B	0.22						50/70 (345/485)	27 (185)	25¹⁾	28	t£2
		C	0.28						55/75 (380/515)	30 (205)	23¹⁾	27	t£2
A515-90	Pressure vessel plates, carbon steel, for intermediate and higher temperature service	55	0.20	0.15/0.40	0.90	0.035	0.035	HR	55/75 (380/515)	30 (205)	23	27	t£1
			0.22
													1<t£2
			0.24
													2<t£4
								N
													4<t£8
			0.26
													t>8
			0.28
		60	0.24	0.15/0.40	0.90	0.035	0.035	HR	60/80 (415/550)	32 (220)	21	25	t£1
			0.27
													1<t£2
			0.29
													2<t£4
								N
													4<t£8
			0.31
													t>8
			0.31
		65	0.28	0.15/0.40	0.90	0.035	0.035	HR	65/85 (450/585)	35 (240)	19	23	t£1
			0.31
													1<t£2
			0.33
													2<t£4
								N
													4<t£8
			0.33
													t>8
			0.33
		70	0.31	0.15/0.40	1.20	0.035	0.035	HR	70/90 (485/620)	38 (260)	17	21	t£1
			0.33
													1<t£2
			0.35
													2<t£4
								N
													4<t£8
			0.35
													t>8
			0.35
A516-90	Pressure vessel plates, carbon steel, for moderate and lower temperature service	55	0.18	0.15/0.40	0.60/0.90²⁾	0.035	0.035	HR	55/75 (380/515)	30 (205)	23	27	t£1/2
			0.20		0.60/1.20			HR or N³⁾					1/2<t£2
			0.22					N					2<t£4
			0.24										4<t£8
			0.26										t>8
		60	0.21	0.15/0.40	0.60/0.90²⁾	0.035	0.035	HR	60/80 (415/550)	32 (220)	21	25	t£1/2
			0.23		0.85/1.20			HR or N³⁾					1/2<t£2
			0.25					N					2<t£4
			0.27										4<t£8
			0.27										t>8
		65	0.24	0.15/0.40	0.85/1.20	0.035	0.035	HR	65/85 (450/585)	35 (240)	19	23	t£1/2
			0.26					HR or N³⁾					1/2<t£2
			0.28					N					2<t£4
			0.29										4<t£8
			0.29										t>8
		70	0.27	0.15/0.40	0.85/1.20	0.035	0.035	HR	70/90 (485/620)	38 (260)	17	21	t£1/2
			0.28					HR or N³⁾					1/2<t£2	Impact Test 冲击试验
			0.30					N					2<t£4	Test Temperature 测试温度 ºF (ºC)	Thickness 厚度 in	Absorbed Energy 冲击功 ft-lbf (J)
			0.31										4<t£8			Average for 3 Specimens	Minimum for 1 Specimen
			0.31										t>8
A516-90	Pressure vessel plates, carbon steel, for moderate and lower temperature service	55LTV	0.18	0.15/0.40	0.60/0.90²⁾	0.035	0.035	N	55/75 (380/515)	30 (205)	23	27	t£1/2	-60 (-51) -50 (-46) -50 (-46) -50 (-46)	t£1 1<t£2 2<t£3 3<t£5	13 (18)	10 (14)
			0.20		0.60/1.20								1/2<t£2
			0.22										2<t£4
			0.24										4<t£8
			0.26										t>8
		60LTV	0.21	0.15/0.40	0.60/0.90²⁾	0.035	0.035	N	60/80 (415/550)	32 (220)	21	25	t£1/2	-60 (-51) -50 (-46) -50 (-46) -50 (-46)	t£1 1<t£2 2<t£3 3<t£5	13 (18)	10 (14)
			0.23		0.85/1.20								1/2<t£2
			0.25										2<t£4
			0.27										4<t£8
			0.27										t>8
		65LTV	0.24	0.15/0.40	0.85/1.20	0.035	0.035	N	65/85 (450/585)	35 (240)	19	23	t£1/2	-60 (-51) -50 (-46) -40 (-40) -25 (-32)	t£1 1<t£2 2<t£3 3<t£5	13 (18)	10 (14)
			0.26										1/2<t£2
			0.28										2<t£4
			0.29										4<t£8
			0.29										8<t
		70LTV	0.27	0.15/0.40	0.85/1.20	0.035	0.035	N	70/90 (485/620)	38 (260)	17	21	t£1/2	-50 (-46) -40 (-40) -30 (-35) -20 (-29)	t£1 1<t£2 2<t£3 3<t£5	15 (20)	12 (16)
			0.28										1/2<t£2
			0.30										2<t£4
			0.31										4<t£8
			0.31										t>8

Notes :

1) See standard for details on concession on certain size ranges.

2) Grade 60 plates ¹/₂ in. (12.5mm) and under in thickness may have 0.85-1.20% manganese on heat analysis.

3) Plates over 1¹/₂ in. thick are normalized.

4) For ASTM A285 and A516, yield stress is determined by either the 0.2% offset method or the 0.5% extension-under-load method.

5) "HR" - hot rolled, "N" - normalized.

BS EN 10028-2 : 1993 Flat products made of steel for pressure purposes

Non-alloy and alloy steel with specified elevated temperature properties

英国标准

(Properties minima unless stated)

Grade 钢号				P235GH	P265GH	P295GH	P355GH	16Mo3	13CrMo4-5	10CrMo9-10	11CrMo9-10
Chemical Composition 化学成份 % maximum 最大			C	0.16	0.20	0.08~0.20	0.10~0.22	0.12~0.20	0.08~0.18	0.08~0.14¹⁾	0.08~0.15¹⁾
			Si	0.35	0.40	0.40	0.60	0.35	0.35	0.50	0.50
			Mn	0.40~1.20	0.50~1.40	0.90~1.50	1.00~1.70	0.40~0.90	0.40~1.00	0.40~0.80	0.40~0.80
			P	0.030	0.030	0.030	0.030	0.030	0.030	0.030	0.030
			S	0.025	0.025	0.025	0.025	0.025	0.025	0.025	0.025
			Cr	0.30	0.30	0.30	0.30	0.30	0.70~1.15	2.00~2.50	2.00~2.50
			Mo	0.08	0.08	0.08	0.08	0.25~0.35	0.40~0.60	0.90~1.10	0.90~1.10
			Ni	0.30	0.30	0.30	0.30	0.30	-	-	-
			Others	⁷⁾⁸⁾	⁷⁾⁸⁾	⁷⁾⁸⁾	⁷⁾⁸⁾	Cu 0.30	Cu 0.30	Cu 0.30	Cu 0.30
Treatment 加工处理				N	N	N	N	N⁵⁾	N+T or Q5	N+T or Q5	N+T or Q5
			Thickness 厚度 (mm)
Yield³⁾ Stress 屈服强度 R_eH N/mm²			t£16	235	265	295	355	275	300	310	310
			16<t£40	225	255	290	345	270	295	300	310
			40<t£60	215	245	285	335	260	295	290	310
			60<t£100	200	215	260	315	240	275	270	310
			100<t£150⁴⁾	185	200	235	295	220	255	250	-
Tensile Strength 抗拉强度 R_m N/mm²			t£16	360/480	410/530	460/580	510/650	440/590	450/600	480/630	520/670
			16<t£40	360/480	410/530	460/580	510/650	440/590	450/600	480/630	520/670
			40<t£60	360/480	410/530	460/580	510/650	440/590	450/600	480/630	520/670
			60<t£100	360/480	410/530	460/580	490/630	430/560	440/590	470/620	520/670
			100<t£150⁴⁾	350/480	400/530	440/570	480/630	420/570	430/580	460/610	-
Elongation 伸长率 A⁵⁾⁶⁾ %			t£40	25	23	22	21	24	20	18	18
			40<t£60	25	23	22	21	23	20	18	18
			60<t£100	24	22	21	20	22	19	17	17
			100<t£150⁴⁾	24	22	21	20	19	19	17	17
Impact¹²⁾ 冲击功 KV J			t£150⁴⁾	27 at 0ºC	27 at 0ºC	27 at 0ºC	27 at 0ºC	-	-	-	-
			t£60	-	-	-	-	31 at 20ºC¹⁴⁾	31 at 20ºC¹⁵⁾	31 at 20ºC	31 at 20ºC¹⁵⁾
			60<t£150⁴⁾	-	-	-	-	27 at 20ºC¹⁴⁾	27 at 20ºC¹⁴⁾	27 at 20ºC	27 at 20ºC¹³⁾¹⁴⁾
Minimum 最小 0.2% proof stress 屈服强度 N/mm²	Temp 温度 ºC	50	t£60 60<t£100 100<t£150	206 191 176	234 207 192	272 249 226	318 298 278	- - -	- - -	- - -	- - -
		100	t£60 60<t£100 100<t£150	190 175 160	215 195 180	250 230 210	290 270 250	- - -	- - -	- - -	- - -
		150	t£60 60<t£100 100<t£150	180 165 155	205 185 175	235 220 200	270 255 240	- - -	- - -	- - -	- - -
		200	t£60 60<t£100 100<t£150	170 160 150	195 175 165	225 210 195	255 240 230	215 200 190	230 220 210	245 225 215	- - -
		250	t£60 60<t£100 100<t£150	150 140 130	175 160 155	205 195 185	235 220 210	200 185 175	220 210 200	230 220 205	255 255 -
		300	t£60 60<t£100 100<t£150	130 125 115	155 145 135	185 180 170	215 200 195	170 165 155	205 195 185	220 210 195	235 235 -
		350	t£60 60<t£100 100<t£150	120 115 110	140 135 130	170 165 155	200 190 175	160 155 145	190 185 175	210 195 185	225 225 -
		400	t£60 60<t£100 100<t£150	110 105 100	130 125 120	155 145 135	180 165 155	150 145 140	180 175 170	200 185 175	215 215 -
		450	t£60 60<t£100 100<t£150	- - -	- - -	- - -	- - -	145 140 135	170 165 160	190 175 165	205 205 -
		500	t£60 60<t£100 100<t£150	- - -	- - -	- - -	- - -	140 135 130	165 160 155	180 165 155	195 195 -

英国标准
BS EN 10028-2 1993 Flat products made of steel for pressure purposes:
Non-alloy and alloy steel with specified elevated temperature properties

(Properties minima unless stated)

Grade 钢号				161-360	161-400	161-430	-	271	281	621	660
Chemical Composition 化学成份 % maximum 最大			C	0.17	0.20	0.25		0.11~0.17	0.08~0.14	0.09~0.17	0.08~0.13
			Si	0.10~0.35	0.10~0.35	0.10~0.35		0.40	0.40	0.50~0.80	0.30
			Mn	0.40~1.20	0.50~1.30	0.60~1.40		1.10~1.50	1.00~1.50	0.40~0.65	0.60~1.00
			P	0.030	0.030	0.030		0.025	0.025	0.025	0.025
			S	0.030	0.030	0.030		0.015	0.015	0.015	0.015
			Cr	0.25	0.25	0.25		0.40~0.70	0.40~0.70	1.00~1.50	0.25~1.50
			Mo	0.10	0.10	0.10		0.24~0.30	0.24~0.30	0.45~0.60	0.50~0.70
			Ni	0.30	0.30	0.30		0.80	0.60~1.00	0.30	0.30
			Cu	0.30⁷⁾	0.30⁷⁾	0.30⁷⁾		0.30	0.30	0.30	0.20
			Al	-	-	-		0.020	0.020	0.020	0.020
			V	-	-	-		0.04~0.12	0.04~0.12	-	0.22~0.28
Treatment 加工处理				AR or N¹¹⁾	AR or N¹¹⁾	AR or N¹¹⁾		N & T	N & T	N & T	N & T
			Thickness 厚度(mm)				Thickness 厚度(mm)
Yield³⁾ Stress 屈服强度 R_eH N/mm²			3<t£16	205	225	250	t£25	500	500	340	-
			16<t£40	195	215	240	25<t£75	460	460	340	-
			40<t£60	185	205	230	75<t£150	430	-	320⁹⁾	-
			60<t£100	175	200	220	100<t£150	-	-	310	-
			100<t£150	170	195	210	t£100	-	-	-	310
Tensile Strength 抗拉强度 R_m N/mm²			3<t£16	360/480	400/520	430/550	t£25	640/760	640/760	515/690	-
			16<t£40	360/480	400/520	430/550	25<t£75	610/730	610/730	515/690	-
			40<t£60	360/480	400/520	430/550	75<t£150	590/690	590/690	500/670⁹⁾	-
			60<t£100	360/480	400/520	430/550	100<t£150	-	-	490/650	-
			100<t£150	360/480	400/520	430/550	t£100	-	-	-	460/610
Elongation 伸长率 A⁵⁾ %			3<t£16	26	24	23	t£25	16	16	18	-
			16<t£40	26	24	23	25<t£75	16	16	18	-
			40<t£63	25	23	22	75<t£150	16	16	16⁹⁾	-
			63<t£100	24	22	21	100<t£150	-	-	16	-
			100<t£150	24	22	21	t£100	-	-	-	-
Impact¹²⁾ 冲击功 KV J			min. average of 3	-	-	-	t£150	27 at 0ºC	27 at -40ºC	-	-
			min. individual	-	-	-	t£150	19 at 0ºC	19 at -40ºC	-	-
			min. average of 3	-	-	-	t£100	-	-	27 at2 0ºC	-
			min. individual	-	-	-	t£100	-	-	19 at 20ºC	-
Minimum 最小 0.2% proof stress 屈服强度 N/mm²	Temp 温度 ºC	100	3<t£16 16<t£40 40<t£63 63<t£100	- - - -	- - - -	- - - -	t£25 25<t£75 75<t£100 100<t£150	420 402 363 363	420 402 363 363	315 315 300 290	282 282 282 -
		150	3<t£16 16<t£40 40<t£63 63<t£100	172 169 158 148	200 192 185 170	222 210 - 186	t£25 25<t£75 75<t£100 100<t£150	406 389 349 349	406 389 349 349	305 305 290 280	276 276 276 -
		200	3<t£16 16<t£40 40<t£63 63<t£100	168 162 152 144	195 185 175 166	215 202 - 181	t£25 25<t£75 75<t£100 100<t£150	398 380 341 341	398 380 341 341	291 291 277 268	267 267 267 -
		250	3<t£16 16<t£40 40<t£63 63<t£100	150 144 141 136	174 165 162 157	192 181 - 172	t£25 25<t£75 75<t£100 100<t£150	389 372 332 332	389 372 332 332	280 280 265 256	241 241 241 -
		300	3<t£16 16<t£40 40<t£63 63<t£100	124 124 124 124	145 145 145 145	161 161 - 161	t£25 25<t£75 75<t£100 100<t£150	374 354 310 310	374 354 310 310	266 266 250 239	225 225 225 -
		350	3<t£16 16<t£40 40<t£63 63<t£100	117 117 117 117	137 137 137 137	153 153 - 153	t£25 25<t£75 75<t£100 100<t£150	363 343 301 301	363 343 301 301	255 255 238 227	216 216 216 -
		400	3<t£16 16<t£40 40<t£63 63<t£100	115 115 115 115	133 133 133 133	148 148 - 148	t£25 25<t£75 75<t£100 100<t£150	351 332 292 292	351 332 292 292	251 251 234 222	209 209 209 -
		450	3<t£16 16<t£40 40<t£63 63<t£100	- - - -	- - - -	- - - -	t£25 25<t£75 75<t£100 100<t£150	347 329 289 289	347 329 289 289	245 245 228 217	203 203 203 -
		500	3<t£16 16<t£40 40<t£63 63<t£100	- - - -	- - - -	- - - -	t£25 25<t£75 75<t£100 100<t£150	314 301 266 266	314 301 266 266	238 238 221 211	200 200 200 -
		550	t£40 40<t£63 63<t£100	- - -	- - -	- - -	t£75 75<t£100 100<t£150	- - -	- - -	227 211 201	197 197 -

Notes : 1), 2), 3), 4), 5), 6), 7), 8), 9), 10), 11), 12), 13), 14), 15) references shall be made to BS EN 10028-2 : 1993 Handbook.

BS EN 10028 - 3 : 1993 Flat products made of steel for pressure purposes

Weldable fine grain steel, normalized.

英国标准

(Properties minima unless stated)

Grade 钢号						P275N	P275NH	P275NL1	P275NL2	P355N	P355NH	P355NL1	P355NL2	P460N	P460NH	P460NL1	P460NL2
Chemical Composition 化学成份 % maximum 最大				C		0.18	0.16	0.16	0.16	0.20	0.20	0.18	0.18	0.20	0.20	0.20	0.20
				Si		0.40	0.40	0.40	0.40	0.50	0.50	0.50	0.50	0.60	0.60	0.60	0.60
				Mn		0.50 ~1.40	0.50 ~1.50	0.50 ~1.50	0.50 ~1.50	0.90 ~1.70	0.90 ~1.70	0.90 ~1.70	0.90 ~1.70	1.00 ~1.70	1.00 ~1.70	1.00 ~1.70	1.00 ~1.70
				P		0.030	0.030	0.030	0.025	0.030	0.030	0.030	0.025	0.030	0.030	0.030	0.025
				S		0.025	0.020	0.020	0.015	0.025	0.025	0.020	0.015	0.025	0.020	0.020	0.015
				Cr		0.30	0.30	0.30	0.30	0.30	0.30	0.30	0.30	0.30	0.30	0.30	0.30
				Mo		0.08	0.08	0.08	0.08	0.08	0.08	0.08	0.08	0.10	0.10	0.10	0.10
				Ni		0.50	0.50	0.50	0.50	0.50	0.50	0.50	0.50	0.80	0.80	0.80	0.80
				Nb		0.050	0.050	0.050	0.050	0.050	0.050	0.050	0.050	0.050	0.050	0.050	0.050
				Ti		0.03	0.03	0.03	0.03	0.03	0.03	0.03	0.03	0.03	0.03	0.03	0.03
				V		0.05	0.05	0.05	0.05	0.10	0.10	0.10	0.10	0.20	0.20	0.20	0.20
				N		0.020	0.020	0.020	0.020	0.020	0.020	0.020	0.020	0.025	0.025	0.025	0.025
				Cu		0.30	0.30	0.30	0.30	0.30	0.30	0.30	0.30	0.70	0.70	0.70	0.70
				Others¹⁾⁴⁾		²⁾	²⁾	²⁾	²⁾	²⁾	²⁾	²⁾	²⁾	³⁾	³⁾	³⁾	³⁾
Treatment 加工处理						N	N	N	N	N	N	N	N	N	N	N	N
				Thickness 厚度(mm)
Yield⁷⁾ Stress 屈服强度 R_eH N/mm²				t£16		275	275	275	275	355	355	355	355	460	460	460	460
				16<t£35		275	275	275	275	355	355	355	355	450	450	450	450
				35<t£50		265	265	265	265	345	345	345	345	440	440	440	440
				50<t£70		255	255	255	255	325	325	325	325	420	420	420	420
				70<t£100		235	235	235	235	315	315	315	315	400	400	400	400
				100<t£150		235	235	235	235	295	295	295	295	380	380	380	380
Tensile Strength 抗拉强度 R_m N/mm²				t£70		390/510	390/510	390/510	390/510	490/630	490/630	490/630	490/630	570/720⁶⁾	570/720⁶⁾	570/720⁶⁾	570/720⁶⁾
				70<t£100		370/490	370/490	370/490	370/490	470/610	470/610	470/610	470/610	540/710	540/710	540/710	540/710
				100<t£150		350/470	350/470	350/470	350/470	450/590	450/590	450/590	450/590	520/690	520/690	520/690	520/690
Elongation⁵⁾⁸⁾ 伸长率 A %				t£70		24	24	24	24	22	22	22	22	17	17	17	17
Elongation⁵⁾⁸⁾ 伸长率 A %				70<t£150		23	23	23	23	21	21	21	21	16	16	16	16
Minimum Impact Value 最小冲击功 for 5 to 150mm thick plate in normalized condition KV J		Temp 温度 ºC		-50	long.	-	27	27	30	-	27	27	30	-	27	27	30
				-50	transv.	-	16	16	27	-	16	16	27	-	16	16	27
				-40	long.	-	34	34	40	-	34	34	40	-	34	34	40
				-40	transv.	-	20	20	30	-	20	20	30	-	20	20	30
				-20	long.	40	47	47	65	40	47	47	65	40	47	47	65
				-20	transv.	20	27	27	40	20	27	27	40	20	27	27	40
				0	long.	47	55	55	90	47	55	55	90	47	55	55	90
				0	transv.	27	34	34	60	27	34	34	60	27	34	34	60
				+20	long.	55	63	63	100	55	63	63	100	55	63	63	100
				+20	transv.	31	40	40	70	31	40	40	70	31	40	40	70
Minimum 最小 0.2% proof stress 屈服强度 N/mm²	Temp 温度 ºC		50	t£35 35<t£70 70<t£100 100<t£150		- - - -	264 247 229 214	- - - -	- - - -	- - - -	336 313 300 280	- - - -	- - - -	- - - -	- - - -	- - - -	- - - -
			100	t£35 35<t£70 70<t£100 100<t£150		- - - -	245 235 216 196	- - - -	- - - -	- - - -	304 294 275 255	- - - -	- - - -	- - - -	402 392 373 353	- - - -	- - - -
			150	t£35 35<t£70 70<t£100 100<t£150		- - - -	226 216 196 176	- - - -	- - - -	- - - -	284 275 255 235	- - - -	- - - -	- - - -	373 363 343 324	- - - -	- - - -
			200	t£35 35<t£70 70<t£100 100<t£150		- - - -	196 196 176 157	- - - -	- - - -	- - - -	245 245 235 216	- - - -	- - - -	- - - -	333 333 324 304	- - - -	- - - -
			250	t£35 35<t£70 70<t£100 100<t£150		- - - -	177 177 157 137	- - - -	- - - -	- - - -	226 226 216 196	- - - -	- - - -	- - - -	314 314 294 275	- - - -	- - - -
			300	t£35 35<t£70 70<t£100 100<t£150		- - - -	147 147 127 108	- - - -	- - - -	- - - -	216 216 196 177	- - - -	- - - -	- - - -	294 294 275 255	- - - -	- - - -
			350	t£35 35<t£70 70<t£100 100<t£150		- - - -	127 127 108 88	- - - -	- - - -	- - - -	196 196 177 157	- - - -	- - - -	- - - -	265 265 245 226	- - - -	- - - -
			400	t£35 35<t£70 70<t£100 100<t£150		- - - -	108 108 88 69	- - - -	- - - -	- - - -	167 167 147 127	- - - -	- - - -	- - - -	235 235 216 196	- - - -	- - - -

Notes : 1), 2), 3), 4), 5), 6), 7), 8) references shall be made to BS EN 10028-3 : 1993 Handbook.

DIN 17155 - EN 10083 HEAT Resistant Plates

德国标准

(Properties minima unless stated)

Grade 钢号	Chemical Composition 化学成份 (ladle analysis) %													Mechanical Properties 机械性能														0.2% Proof Stress (hot yield stress) 屈服强度 (热)
	C	Si	Mn	P max	S max	Al_total	Cr	Cu max	Mo	Nb max	Ni max	Ti max	V max	Upper Yield Stress 屈服强度 (transv.)					Tensile Strength 抗拉强度 (transverse)			Elongation 伸长率 (L_o=5d_o) (transverse)		Impact Test 冲击功 (ISO-V transverse) mean value from 3 spec.				Thickness 厚度 t mm	at temperature 温度 ºC
														thickness 厚度 t(mm)					thickness 厚度 t(mm)			thickness 厚度 t(mm)		thickness 厚度 t(mm)					200	250	300	350	400	450	500
														t£16	16<t £40	40<t £60	60<t £100	100<t £150	t£60	60<t £100	100<t £150	t£60	60<t £150	t£60	60<t £150	t£60	60<t £150		200	250	300	350	400	450	500
														N/mm²					N/mm²			%		at 0ºC		at +20ºC			N/mm²
														N/mm²					N/mm²			%		J		J			N/mm²
H II	£0.20	£0.35	0.50 ~1.30	0.035	0.030	³0.02	¹⁾²⁾ £0.25	¹⁾²⁾ 0.30	¹⁾²⁾ £0.10	¹⁾ 0.01	¹⁾²⁾ 0.30	¹⁾ 0.03	¹⁾ 0.03	265	255	245	215	200	410 to 530	410 to 530	400 to 530	22	21	31	31	-	-	t£60 60<t£100 100<t£150	205 195 185	185 175 165	155 145 135	140 135 130	130 125 120	125 120 115	- - -
17 Mn 4	0.14 ~0.20	£0.40	0.90 ~1.40	0.035	0.030	³0.02	¹⁾²⁾ £0.25	¹⁾²⁾ 0.30	¹⁾²⁾ £0.10	¹⁾ 0.01	¹⁾²⁾ 0.30	¹⁾ 0.03	¹⁾ 0.03	290	285	280	255	230	460 to 580	450 to 570	440 to 570	21	20	31	31	-	-	t£60 60<t£100 100<t£150	245 230 215	225 210 195	205 190 175	175 165 155	155 135 135	135 115 115	- - -
15 Mo 3	0.12 ~0.20	0.10 ~0.35	0.40 ~0.90	0.035	0.030	³⁾	£0.25¹⁾	0.30¹⁾	0.25 ~0.35	-	0.30¹⁾	-	-	275⁴⁾	270	260	240	220	440 to 590	430 to 580	420 to 570	20	19	-	-	31	27	t£10 10<t£40 40<t£60 60<t£100 100<t£150	240 225 210 200 190	220 205 195 185 175	195 180 170 160 150	185 170 160 155 145	175 160 150 145 140	170 155 145 140 135	165 150 140 135 130
13 CrMo 4 4	0.08 ~0.18	0.10 ~0.35	0.40 ~1.00	0.035	0.030	³⁾	0.70 ~1.10	0.30¹⁾	0.40 ~0.60	-	-	-	-	300	295	295	275	255	440 to 590	430 to 580	420 to 570	20	19	-	-	31	27	t£10 10<t£40 40<t£60 60<t£100 100<t£150	255 240 230 220 210	245 230 220 210 200	230 215 205 195 185	215 200 190 185 175	205 190 180 175 170	195 180 170 165 160	190 175 165 160 155
10 CrMo 9 10	0.06 ~0.15	£0.50	0.40 ~0.70	0.035	0.030	³⁾	2.00 ~2.50	0.30¹⁾	0.90 ~1.10	-	-	-	-	310	300	290	270	250	480 to 630	460 to 630	460 to 630	18	17	-	-	31	27	t£40 40<t£60 60<t£100 100<t£150	245 235 225 215	240 230 220 210	230 220 210 200	215 205 195 185	205 195 185 175	195 185 175 165	185 175 165 155
ASt 41	<0.20	<0.35	³0.45	0.045	0.045	-	£0.3	-	-	-	-	-	-	265	255	245	215	200	410 to 530	410 to 530	400 to 530	22	21	DVM transv. aged				t£60 60<t£100 100<t£150	205 195 185	185 175 165	155 145 135	140 135 130	130 125 120	125 120 115	- - -
																								-	-	27	-
																								DVM transv. non-aged
																								31	-	-	-

Notes :

1) Proof of compliance with these limit values required only if specially agreed.

2) The total mass content of Cr, Cu, Mo and Ni must not exceed 0.70%.

3) The Al content of the melt is to be determined and stated in the certificate.

4) Thickness £ 10mm is subject to a minimum value of 285 N/mm².

5) Hot tensile test at 300ºC, per melt.

Go To

Content on this page requires a newer version of Adobe Flash Player.

Pressure Vessels plates
ASTM, BS EN, DIN

Content on this page requires a newer version of Adobe Flash Player.

Content on this page requires a newer version of Adobe Flash Player.

Pressure Vessels plates ASTM, BS EN, DIN

Content on this page requires a newer version of Adobe Flash Player.

Pressure Vessels plates
ASTM, BS EN, DIN